THE EFFECT OF ANNEALING TEMPERATURES AFTER THERMOMECHANICAL PROCESS TO THE CORROSION BEHAVIOR OF Ni3(Si,Ti) IN SULFATE SOLUTION

International Journal of Science and Engineering

Yasuyuki Kaneno¹  Gadang Priyotomo² 

[1] Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University1-1 Gakuen-cho, Sakai, Osaka;Research Center for Metallurgy and Material, Indonesian Institute of Sciences, Serpong, Tangerang;

关键词: Intermetallic Compound;    Immersion Test;    Polarization Curve;    Sulfate ion;    Corrosion;   

DOI  :  10.12777/ijse.8.2.141-145

来源: DOAJ

【 摘 要 】

The corrosion behaviour of the intermetallic compounds Ni3(Si,Ti) (L12: single phase), has been investigated using an immersion test, polarization method, scanning electron microscope in 0.5 kmol/m3 H2SO4 solution at 303 K.  Moreover, the corrosion behaviour of austenitic stainless steel type 304 was studied under the same experimental conditions as reference. It was found that the intergranular attack and uniform attack were observed on Ni3(Si,Ti) after thermomechanical and annealing processes (1173K and 1273K) respectively in the immersion test. From the immersion test and polarization curves, all annealed Ni3(Si,Ti) had less corrosion resistance compared to type 304. In addition, Ni3(Si,Ti) was difficult to form a stable passive film, but not for type 304.

【 授权许可】

Unknown