Towards the Enhancement in Photocatalytic Performance of Ag3PO4 Nanoparticles through Sulfate Doping and Anchoring on Electrospun Nanofibers

Nanomaterials

Gopal Panthi¹  Mira Park¹  Kapil Raj Gyawali² 

[1] Department of Biomedical Sciences and Institute for Medical Science, Jeonbuk National University, Jeonju 54907, Korea;Department of Chemistry, Birendra Multiple Campus, Tribhuvan University, Bharatpur 442000, Chitwan, Nepal;

关键词: electrospinning;    SO₄²⁻Ag₃PO₄ nanoparticles;    organic dyes;    photocatalyst;    visible light;   

DOI  :  10.3390/nano10050929

来源: DOAJ

【 摘 要 】

Present work reports the enhancement in photocatalytic performance of Ag₃PO₄ nanoparticles through sulfate doping and anchoring on Polyacrylonitrile (PAN)-electrospun nanofibers (SO₄²⁻-Ag₃PO_4/PAN-electrospun nanofibers) via electrospinning followed by ion-exchange reaction. Morphology, structure, chemical composition, and optical properties of the prepared sample were characterized using XRD, FESEM, FTIR, XPS, and DRS. The anchoring of SO₄²⁻-Ag₃PO₄ nanoparticles on the surface of PAN-electrospun nanofibers was evidenced by the change in color of the PAN nanofibers mat from white to yellow after ion-exchange reaction. FESEM analysis revealed the existence of numerous SO₄²⁻-Ag₃PO₄ nanoparticles on the surface of PAN nanofibers. Photocatalytic activity and stability of the prepared sample was tested for the degradation of Methylene blue (MB) and Rhodamine B (RhB) dyes under visible light irradiation for three continuous cycles. Experimental results showed enhanced photodegradation activity of SO₄²⁻-Ag₃PO₄/PAN-electrospun nanofibers compared to that of sulfate undoped sample (Ag₃PO₄/PAN-electrospun nanofibers). Doping of SO₄²⁻ into Ag₃PO₄ crystal lattice could increase the photogenerated electron–hole separation capability, and PAN nanofibers served as support for nanoparticles to prevent from agglomeration.

【 授权许可】

Unknown