Investigation of the Impact Strength of the Epoxy-Polyester Material for Using in Aggressive Environments in the Water Transport

Communications

Abdellah Menou¹  Oleksandr Sapronov²  Andriy Buketov²  Serhii Yakushchenko²  Anna Sapronova²  Mykola Brailo² 

[1] International Academy of Civil Aviation, Casablanca, Morocco;Kherson State Maritime Academy, Kherson, Ukraine;

关键词: epoxy-polyester composite;    impact strength;    crack initiation;    main crack;    impact load;    ir-spectral analysis;   

DOI  :  10.26552/com.C.2021.4.B346-B353

来源: DOAJ

【 摘 要 】

The influence of the aggressive environments of river water, seawater, oil, petrol and sodium hydroxide on the impact strength of epoxy-polyester composite was investigated. Testing was conducted by two different methods. It was determined that the impact strength of specimens that were kept at air was W' = 4.2 kJ/m2 (by the second method - W'' = 7.0 kJ/m2). The energy spent on destruction of the control specimen was E = 0.92 J. The main regularities of the crack propagation process in the studied material were found and qualitatively described. The time of a crack propagation (τ = 0.16 μs) was determined. The maximum load, which leads to destruction of the specimen was Pmax = 2.47 kN. The comparative analysis of investigated specimens was conducted by the IR-spectroscopy method. It was found, that the biggest decrease in material properties was observed for the specimen that was kept in the petrol environment.