Influence of the Die Height on the Density of the Briquette Produced from Shredded Logging Residues

Materials

卷:14

Arkadiusz Gendek¹  Magdalena Dąbrowska¹  Tomasz Nurek¹ 

[1] Department of Biosystems Engineering, Institute of Mechanical Engineering, Warsaw University of Life Sciences–SGGW, Nowoursynowska 164, 02-787 Warsaw, Poland;

关键词: die height;    biomass compaction;    relaxation coefficient;    briquette density;    logging residues;    mechanical engineering;   

DOI  :  10.3390/ma14133698

来源: DOAJ

【 摘 要 】

An alternative to plant biomass of various origins are forest logging residues. They differ significantly from other, previously used plant materials. This difference is due to the heterogeneous composition and relatively large size of individual particles. This research on the compaction of this type of shredded material was aimed at determining the influence of the die height on the density and relaxation of briquettes. This parameter is crucial for the proper construction of compaction devices. The measurements were carried out for the same fractional composition of the shredded logging residues, with variable input parameters of the material and process. It was found that the briquette density and relaxation are influenced by the die height, as well as the material moisture content and process temperature. The highest density at maximum compaction pressure (1.40 g·cm^–3) was obtained at a moisture content of 16%, temperature of 80 °C, and the lowest die height (195 mm). In the case of the briquette density after ejection from the die, the best results were obtained at the same temperature and die height but at a moisture content of 9%. The tests confirmed that, regardless of the process temperature and material moisture, the briquette density increases as the die height is reduced. The relaxation coefficient of compacted logging residues ranges from 21.7% to 50.1% and depends mainly on the material moisture content and the temperature of the process. The lowest value of the relaxation coefficient (21.7 ± 1.61) was obtained at 9% moisture content, 60 °C temperature, and 220 mm die height.

【 授权许可】

Unknown