Microstructural evolution and performance of carbon fiber-toughened ZrB2 ceramics with SiC or ZrSi2 additive

Journal of Advanced Ceramics

卷:7

Ping Hu¹  Zhongjia Huang²  Gang Wang²  Fangyu Liu²  Kaixuan Gui² 

[1] National Key Laboratory of Science and Technology on Advanced Composites in Special Environments, Harbin Institute of Technology;

[2] School of Materials Science and Engineering, Anhui Polytechnic University;

关键词: carbon fibers;    microstructural evolution;    hot pressing;    thermal shock resistance;    oxidation resistance;   

DOI  :  10.1007/s40145-018-0284-2

来源: DOAJ

【 摘 要 】

Abstract ZrB2–SiC/ZrSi2 ceramics containing 30 vol% carbon fiber (Cf) additive were fabricated by hot pressing at low temperature (1500 °C) using submicron ZrB2 powders, and their microstructural evolution and performance were investigated. The addition of SiC or ZrSi2 significantly reduced the onset sintering temperature and enhanced the densification of ZrB2. ZrB2–ZrSi2–Cf showed poor performance owing to the serious fiber degradation, while the fiber degradation was effectively inhibited in ZrB2–SiC–Cf resulting in high fracture toughness, substantial fiber pull-out, and non-brittle fracture mode for such material. The critical thermal shock temperature difference of ZrB2–SiC–Cf was up to 741 °C, significantly higher than those of ZrB2–SiC/ZrSi2 and ZrB2–ZrSi2–Cf. Moreover, this composite displayed a good oxidation resistance at 1500 °C in air.