Wettability Characteristics of Laser Surface Textured Plasma Sprayed TiO2/ZnO Coatings

Tribology Online

卷:14

Yusliza Yusuf¹  Mariyam Jameelah Ghazali¹  Kiyoshi Ohnuma²  Susumu Nakamura³  Yuichi Otsuka⁴  Mohd Fadzli Bin Abdollah⁵  Sarita Morakul⁶ 

[1] Centre for Materials Engineering and Smart Manufacturing, Faculty of Engineering and Built Environment, Universiti Kebangsaan Malaysia;

[2] Department of Bioengineering, Nagaoka University of Technology;

[3] Department of Electrical and Electronic Systems Engineering, National Institute of Technology, Nagaoka College;

[4] Department of System Safety, Nagaoka University of Technology;

[5] Fakulti Kejuruteraan Mekanikal , Universiti Teknikal Malaysia Melaka;

[6] Graduate School of Material Science, Nagaoka University of Technology;

关键词: laser surface texturing;    tio2/zno coating;    wettability;    self-cleaning;   

DOI  :  10.2474/trol.14.279

来源: DOAJ

【 摘 要 】

Surface wettability behaviour is generally categorised as hydrophobic and hydrophilic depending on the contact angle value. Surface wettability has been attracting considerable attention in research due to its unique behaviour in the field of self-cleaning, anti-fouling and anti-corrosion. Surfaces with high and low wettabilities can be fabricated using various methods, including chemical etching, anodisation and laser surface texturing. The present study investigated the effects of textured surfaces via laser surface texturing on the wettability properties of TiO2/ZnO coatings. TiO2/ZnO coating was selected due to its high photocatalytic activity, non-toxicity and low cost, which are essential properties for self-cleaning and anti-fouling applications. Picosecond laser ablation was used to produce micro- dimple textures on the coating surfaces. The wettability of the laser-textured surfaces was greatly reduced, achieving superhydrophilic properties with contact angle of 1.4° ± 2.42° for laser-textured TiO2 coating. On the other hand, coatings with ZnO compositions exhibited increased contact angles for both textured and non-textured surfaces. Moreover, no clear cut correlations between the surface roughness properties of non-textured and laser-textured TiO2/ZnO coatings and the surface wettability properties was observed. This finding provides new approaches in designing textured surface materials that can effectively increase the wettability properties for self-cleaning and anti-fouling applications.