Comparative Research of Microstructure and Mechanical Properties of Stainless and Structural Steel Dissimilar Welds | |
Regita Bendikiene1  Antanas Ciuplys1  Jolanta Baskutiene1  Saulius Baskutis1  Karolis Dutkus2  | |
[1] Department of Production Engineering, Faculty of Mechanical Engineering and Design, Kaunas University of Technology, Studentu Str. 56, LT-51424 Kaunas, Lithuania; | |
[2] Umega Group AB, Kauno Str. 120, LT-20115 Ukmerge, Lithuania; | |
关键词: stainless steel; metal inert gas welding; dissimilar welds; microstructure; mechanical properties; | |
DOI : 10.3390/ma14206180 | |
来源: DOAJ |
【 摘 要 】
The present study utilized a metal inert gas welding (MIG) to make a dissimilar weld of stainless steel AISI 304, 314, 316L, 420 grades and a standard structural steel S355MC. It refers to a weld joining two materials from different alloy systems commonly used in heat exchangers, pressure vessels, and power plant systems. Obviously, maintaining the integrity of such welds is of paramount importance to the safety issues. Therefore, detailed microscopic and experimental studies were performed to evaluate the reliability of these welds. The microscopic analysis did not reveal any presence of weld defects such as porosity or cracks, which ensured that MIG process parameters were properly selected. The performance of dissimilar welds was assessed by hardness and tensile tests. The hardness profiles revealed differences between austenitic and martensitic steel welds that later showed extremely high values in the heat-affected zone (HAZ), which caused fractures in this zone during tensile test. The welds of all austenitic steel grades withstood the tensile test, showing an average tensile strength of 472 MPa with fractures observed in the base metal zone. It made clear that the use of a filler rod 308LSI is suitable only for the austenitic stainless and structural steel dissimilar welds and not appropriate for martensitic-structural steel welds. The achieved results revealed that the higher hardness of the martensitic phase in the HAZ of AISI 420 is closely related with the formation of untempered coarse martensitic structure and higher carbon content.