Durability of Bridge Structural Elements

Communications

卷:18

Josef Vican¹  Peter Kotes¹ 

[1] Department of Structures and Bridges, Faculty of Civil Engineering, University of Zilina, Slovakia;

关键词: corrosion;    corrosion models;    cross-sectional resistance;    numerical analyses;    design for durability;   

DOI  :  10.26552/com.C.2016.4.61-67

来源: DOAJ

【 摘 要 】

Due to environmental actions evocated by the atmospheric behaviour, the material degradation processes are started. The effects of material deterioration due to corrosion cause the loss of cross-sectional or member resistance, but the limit state method does not directly reflect design and verification allowing for failures caused by this influence. The time-variant loss of steel and reinforced concrete moment cross-sectional resistances were computed respecting specific corrosion models to express the time-dependent approximation function taking into account effects of corrosion degradation. The paper presents the general principles of structural elements design for durability based on the limit state concept and their application in the case of moment cross-sectional resistance respecting the effects of corrosion degradation.

【 授权许可】

Unknown