Influence of Glazed Hollow Bead on the Performance of Polyvinyl Alcohol Fiber Reinforced Cement Composites

Crystals

卷:12

Yadi Zhao¹  Jie Dai¹  Yunfei Li¹  Xuesen Li¹ 

[1] School of Civil Engineering, Henan University of Technology, Zhengzhou 450001, China;

关键词: polyvinyl alcohol fiber;    glazed hollow bead;    mechanical properties;    thermal conductivity;    micro-structure;   

DOI  :  10.3390/cryst12040454

来源: DOAJ

【 摘 要 】

To improve the thermal insulation properties and toughness of concrete, the glazed hollow bead (GHB) and polyvinyl alcohol (PVA) fiber reinforced cementitious composites (GPCC) were investigated by orthogonal test, which includes six GHB mass percentage (20%, 40%, 60%, 80%,100%, 120%), three PVA volume fraction (1%, 1.5%, 2%) and water binder ratio (0.26, 0.30, 0.34). Compressive, split tensile strengths and thermal conductivity of GHB-PVA reinforced cementitious composites (GPCC) were tested, and the mechanism of fibers was analyzed from a microscopic perspective. The results revealed that the thermal insulation will be significantly improved with the increased content of GHB, but the compressive and split tensile strength will be decreased simultaneously. No obvious effect was found by the PVA fiber addition on its strength indexes, and the presence of GHB will affect the bridging action of PVA fibers. The water binder ratio has more effect on strengths than thermal conductivity. Based on the mechanical performance rather than the thermal insulation analysis test, the optimal mix proportions were proposed: mass percentage of 40% GHB, a volume fraction of 1.5% PVA fiber, and 0.26 water-binder ratio. Moreover, the anchoring and bridging effect of PVA fibers will effectively balance the stress generated by the shrinkage of cement paste, and inhibits or even prevents the development of cracks. However, a certain number of tiny cracks will be formed near the GHB, and between GHB and PVA fibers, which will cause local stretching and peeling of PVA, and shattering inside the GHB with the increase of external force. The findings of this study can provide a useful reference for the application of an insulated-bearing material with GHB and PVA fiber.

【 授权许可】

Unknown