Friction Spot Lap Joining of Aluminum Alloy AA6061 to Pre-Holed and Threaded Carbon Steel AISI 1006 | |
Ibrahim H.K.1  Hussein S.K.1  Jadee K.J.1  | |
[1] Engineering Technical College - Baghdad, Middle Technical University, Baghdad, Iraq; | |
关键词: aa6061; aisi 1006; friction spot joining; aluminum extrusion; | |
DOI : 10.2478/ijame-2022-0005 | |
来源: DOAJ |
【 摘 要 】
This work addresses to joining aluminum alloy AA6061 to carbon steel AISI 1006 sheets using the friction spot joining technique. The steel sheets were pre-holed and threaded with an internal M6 thread. The joining process was carried out by extruding the aluminum through the steel hole and thread using a rotating tool with friction between the tool and aluminum. Three process parameters were used: pre-heating time, rotating speed and plunging depth of the tool, with four levels for each parameter. The results indicated that the two materials joined by a micro-scale mechanical interlock at an interface line of a width ranged between 0.7 to ~ 2.5 mm. The joint’s shear force reached a minimum and maximum value of 2000 and 2500 N, respectively. The plunging depth was the most effective factor affecting the amount of the extruded aluminum and the joint’s shear force.
【 授权许可】
Unknown