Obtención de microestructuras de grano ultrafino en aleaciones de aluminio mediante extrusión en canal angular (ECAE)

Boletín de la Sociedad Española de Cerámica y Vidrio

卷:43

关键词: Equal-channel angular extrusion (ECAE);    Microhardness;    Texture;    EBSD;    Ultrafine grained (UFG) structures;    Extrusión en canal angular (ECAE);    Microdureza;    Textura;    EBSD;    Estructuras de grano ultrafino;   

DOI  :  

来源: DOAJ

【 摘 要 】

Al 5083 samples have been subjected to 90º equal-channel angular extrusion (ECAE) at 270ºC. After ECAE, the microhardness was measured and the texture for the plane perpendicular to the extrusion direction was analysed by X-Rays and EBSD. The microstructure was characterized by optical microscopy and EBSD. As deformation accumulates the hardness increases until it reaches saturation at an effective strain of about ε∼4. With regard to the texture, it has been shown that a high density of {111} planes are oriented parallel to the shear plane of the last pass.

Varias muestras de aluminio 5083 se han sometido a extrusiones en canal angular de 90º a 270ºC. A continuación se midieron las durezas de las muestras obtenidas y se caracterizó la textura en el plano perpendicular a la dirección de extrusión mediante Rayos-X y difracción de electrones retrodispersados (EBSD). La caracterización microestructural se hizo mediante microscopio óptico y EBSD. Se ha observado que la dureza aumenta sensiblemente con el grado de deformación y que alcanza un nivel máximo de saturación a partir de ε∼4. En cuanto a la textura, se observa que los planos {111} tienden a orientarse paralelos al plano de la última cortadura.

【 授权许可】

Unknown