Síntesis y Caracterización de Ag2Cu2O3, el primer óxido de cobre y plata

Boletín de la Sociedad Española de Cerámica y Vidrio

卷:39

关键词: Copper;    oxygen;    silver;    solid-state structures;    superconductors;    Cobre;    oxígeno;    plata;    estructuras estado-sólido;    superconductores;   

DOI  :  

来源: DOAJ

【 摘 要 】

Despite the crystal-chemical similarities between copper and silver ions, there is no known silver copper oxide, neither natural nor synthetic. In this work, we present the synthesis at room-temperature of the first silver copper oxide of formula Ag2Cu2O3 (tetragonal, a=5.8857(3)Å, c=10.6868(7)Å, space group I41/amd, Z=4). It should be noted that the thermal stability of this new oxide is enhanced with respect to Ag2O or even CuO. The structure consists of alternating chains of edge-sharing square planar Cu(II) and zigzag chains of linearly coordinated Ag(I) ions.

A pesar de las similitudes cristaloquímicas entre los iones de cobre y los de plata, no existe ningún óxido mixto de cobre y plata ni natural ni sintético. En este trabajo se presenta la síntesis a bajas temperaturas del primer óxido mixto de cobre y plata, de fórmula Ag2Cu2O3 (tetragonal, a=5.8857(3)Å, c=10.6868(7)Å, grupo espacial I41/amd, Z=4). Este óxido posee una estabilidad térmica superior a los correspondientes óxidos de cobre y de plata. Contiene cadenas de iones Cu(II) cuadrado-planos que alternan con cadenas en zig-zag de Ag(I) con coordinación lineal.

【 授权许可】

Unknown