期刊论文详细信息
Journal of Asian Ceramic Societies 卷:4
Fabrication of gadolinium hydroxide nanoparticles using ion-exchange resin and their MRI property
Y. Kobayashi1  H. Morimoto1  K. Gonda2  Y. Kubota2  N. Ohuchi3  T. Nakagawa3 
[1] Department of Biomolecular Functional Engineering, College of Engineering, Ibaraki University, Naka-narusawa-cho, Hitachi, Ibaraki 316-8511, Japan;
[2] Department of Medical Physics, Graduate School of Medicine, Tohoku University, Sendai, Miyagi 980-8575, Japan;
[3] Department of Nano-Medical Science, Graduate School of Medicine, Tohoku University, Seiryo-machi, Aoba-ku, Sendai 980-8575, Japan;
关键词: Gadolinium hydroxide;    Nanoparticle;    Anion exchange resin;   
DOI  :  10.1016/j.jascer.2016.01.005
来源: DOAJ
【 摘 要 】

This paper describes a method to fabricate gadolinium hydroxide (Gd(OH)3) nanoparticles. An opaque solution was prepared by adding basic anion exchange resin (BAER) to a Gd(NO3)3 aqueous solution at room temperature and aging the solution for 12–24 h; the solution became basic because of the exchange of H2O with OH−. The particles in the opaque solution have a needle structure, and their crystal structure was hexagonal Gd(OH)3. Their longitudinal and lateral average particle sizes tend to increase in the ranges of 175.0–222.1 and 33.9–52.3 nm when the aging time increases from 12 to 24 h, respectively. The relaxivity value for T1-weighted imaging was 0.79 mM−1 s−1 for the solution that was prepared at the aging time of 18 h, which was ca. 20% of that for a commercial Gd complex contrast agent.