Preheated (Heat-Assisted) Clinching Process for Al/CFRP Cross-Tension Specimens | |
Pai-Chen Lin1  Jun-Chang Fang1  Jia-Wei Lin1  Yern-Chee Ching2  XuanVan Tran3  | |
[1] Advanced Institute of Manufacturing with High-tech Innovations & Department of Mechanical Engineering, National Chung-Cheng University, Chiayi 62102, Taiwan; | |
[2] Department of Chemical Engineering, University of Malaya, Kuala Lumpur 50603, Malaysia; | |
[3] Institute of Development of Strategy, Thu Dau Mot University, Phu Hoa Ward, Thu Dau Mot City 0650, Vietnam; | |
关键词: clinching; joining composite; modifications of clinching joining technologies; carbon-fiber-reinforced-plastic; aluminum alloy; fatigue; | |
DOI : 10.3390/ma13184170 | |
来源: DOAJ |
【 摘 要 】
Effects of processing parameters on preheated (heat-assisted) clinching process to join aluminum alloy 5052-H32 (AA5052) and thermoplastic carbon-fiber-reinforced-plastic (TP-CFRP) sheets for cross-tension (CT) specimens were first studied. Preheating was critical since brittle TP-CFRP could be softened to avoid fracturing or cracking during clinching process. Four processing parameters, including punching force, die depth, heating mode, and heating temperature, were considered. Quasi-static tests and microscope observations were taken to evaluate AA5052/TP-CFRP clinch joints in CT specimens and determine appropriate processing parameters for fatigue tests. Finally, fatigue data and failure mode of clinch joints in CT specimens were obtained and discussed.