Synthesis of Gd+3 doped hydroxyapatite ceramics: optical, thermal and electrical properties | |
Fatih Akkurt1  Ebru Saban2  Bilal Demirel2  Ali Yaras3  | |
[1] Department of Chemical Engineering, Gazi University, Ankara, Turke;Department of Material Science and Engineering, Erciyes University, Kayseri, Turke;Department of Metallurgy and Materials Engineering, Bartin University, Bartin, Turke; | |
关键词: optical properties; thermal conductivity; electrical resistance; hydroxyapatite (HAp); | |
DOI : 10.1080/21870764.2021.1920160 | |
来源: Taylor & Francis | |
【 摘 要 】
In this study, hydroxyapatite powder Ca10(PO4)6(OH)2 (HAp) doped with gadolinium (Gd3+) (HAp:Gd3+) in different mole percentage of between 0.1 and 1.6 was synthesized by sol−gel method at 900°C. The reaction was carried out by hydrolysis of Ca(OH)2 and DCPD (CaHPO4.2H2O) in aqueous solution and then analyzed through XRD, SEM, FTIR, TGA and Four-Point Probe method (custom-made). The results show that Gd3+ has been successfully doped into the hydroxyapatite structure. Then, the photoluminescence, thermal and electrical properties of pure and Gd3+ doped hydroxyapatite were studied and compared with the pure hydroxyapatite. In conclusion, the emission band of Ca10-xGdx(PO4)6(OH)2 was observed at 263, 278, 294, 312 nm) under excitation with 185 nm. The Stokes shift of HAp:Gd3+ was calculated to be 16.031 cm−1. On the other hand, the electrical and thermal conductivity of HAp increased with the increase in Gd3+ concentration due to Ca2+ cation vacancies caused by Gd3+doping.
【 授权许可】
CC BY
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO202111266643579ZK.pdf | 5259KB | download |