Enhanced flexural properties of aramid fiber/epoxy composites by graphene oxide | |
article | |
Yinqiu Wu1  Bolin Tang1  Kun Liu1  Xiaoling Zeng1  Jingjing Lu1  Tongtong Zhang1  Xiaojun Shen1  | |
[1] Key Laboratory of Yarn Materials Forming and Composite Processing Technology of Zhejiang Province, Jiaxing University;School of Materials Science and Engineering, Changzhou University | |
关键词: graphene oxide; aramid fiber; flexural properties; interfacial bonding; | |
DOI : 10.1515/ntrev-2019-0043 | |
学科分类:社会科学、人文和艺术(综合) | |
来源: De Gruyter | |
【 摘 要 】
The reinforcing effect of graphene oxide (GO) in enhancing the flexural strength and flexural modulus of aramid fiber (AF)/epoxy composites were investigated with GO-AFs at a weight fraction of 0.1-0.7%. The flexural strength and flexural modulus of the composite reached 87.16 MPa and 1054.7 MPa, respectively, which were about 21.19% and 40.86% higher than those of the pure epoxy resin, respectively. In addition, the flexural properties and interfacial shear strength (IFSS) of composite reinforced by GO-AFs were much higher than the composites reinforced by AFs due to GO improved the interfacial bonding between the reinforcement material and matrix.