Microstructure and wear behavior of Al-Al 2 O 3 in situ composites fabricated by the reaction of V 2 O 5 particles in pure aluminum
article
Amneesh Singla1  Rajnish Garg1  Mukesh Saxena1 
[1] Department of Mechanical Engineering, College of Engineering Studies, University of Petroleum and Energy Studies
关键词: alumina;    hardness;    in situ composite;    V2O5;    wear;   
DOI  :  10.1515/gps-2015-0073
来源: De Gruyter
PDF
【 摘 要 】

In this study, fabrication of Al based in situ composites and their formation mechanism is investigated through the stir casting approach. In situ composites were prepared with the addition of various amounts of V 2 O 5 particles in pure aluminum. Due to the reaction of vanadium pentoxide with the molten aluminum, Al 2 O 3 (alumina) is formed. X-ray diffraction (XRD), scanning electron microscopy (SEM) and microscopy were used for the examination of the produced in situ composites. Increment in hardness was observed in cast in situ composites as compared to the pure aluminum. Friction and wear behaviors of cast in situ composites were studied by using a pin on disc tribo tester. The investigation showed that the wear loss and coefficient of friction increases with the load. The result indicates that wear rate increases with higher percentage of addition. The different phases formed are shown by the XRD study and the presence of Al 3 V and alumina in the composite enhanced the properties.

【 授权许可】

CC BY   

【 预 览 】
附件列表
Files Size Format View
RO202107200001839ZK.pdf 3250KB PDF download
  文献评价指标  
  下载次数:7次 浏览次数:1次