Nickel–Cobalt Hydroxides with Tunable Thin-Layer Nanosheets for High-Performance Supercapacitor Electrode

Nanoscale Research Letters

Yuefeng Zhao¹  Shaobo Liu²  Yishan Zhou²  Luomeng Zhang²  Hui Xia²  Wenke Xie² 

[1] Collaborative Innovation Center of Light Manipulations and Applications, Shangdong Normal University, 250358, Jinan, China;School of Physics and Electronics, Central South University, 410083, Changsha, China;

关键词: Hydrothermal method;    Nickel–cobalt double hydroxides;    Nanosheets;    High performance;    Supercapacitor;   

DOI  :  10.1186/s11671-021-03543-w

来源: Springer

【 摘 要 】

Layered double hydroxides as typical supercapacitor electrode materials can exhibit superior energy storage performance if their structures are well regulated. In this work, a simple one-step hydrothermal method is used to prepare diverse nickel–cobalt layered double hydroxides (NiCo-LDHs), in which the different contents of urea are used to regulate the different nanostructures of NiCo-LDHs. The results show that the decrease in urea content can effectively improve the dispersibility, adjust the thickness and optimize the internal pore structures of NiCo-LDHs, thereby enhancing their capacitance performance. When the content of urea is reduced from 0.03 to 0.0075 g under a fixed precursor materials mass ratio of nickel (0.06 g) to cobalt (0.02 g) of 3:1, the prepared sample NiCo-LDH-1 exhibits the thickness of 1.62 nm, and the clear thin-layer nanosheet structures and a large number of surface pores are formed, which is beneficial to the transmission of ions into the electrode material. After being prepared as a supercapacitor electrode, the NiCo-LDH-1 displays an ultra-high specific capacitance of 3982.5 F g−1 under the current density of 1 A g−1 and high capacitance retention above 93.6% after 1000 cycles of charging and discharging at a high current density of 10 A g−1. The excellent electrochemical performance of NiCo-LDH-1 is proved by assembling two-electrode asymmetric supercapacitor with carbon spheres, displaying the specific capacitance of 95 F g−1 at 1 A g−1 with the capacitance retention of 78% over 1000 cycles. The current work offers a facile way to control the nanostructure of NiCo-LDHs, confirms the important affection of urea on enhancing capacitive performance for supercapacitor electrode and provides the high possibility for the development of high-performance supercapacitors.