Improving Cyclability of Lithium Metal Anode via Constructing Atomic Interlamellar Ion Channel for Lithium Sulfur Battery

Nanoscale Research Letters

Nan Jue¹  Yuanfu Chen¹  Yong Wang¹  Mao Yang¹ 

[1] State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, 610054, Chengdu, China;

关键词: Lithium sulfur batteries;    Lithium dendrites;    Interlamellar ion channel;    Layered silicate clay;    Nano composites;   

DOI  :  10.1186/s11671-021-03508-z

来源: Springer

【 摘 要 】

Uniform migration of lithium (Li) ions between the separator and the lithium anode is critical for achieving good quality Li deposition, which is of much significance for lithium metal battery operation, especially for Li–sulfur (Li–S) batteries. Commercial separators such as polypropylene or polyethylene can be prepared by wet or dry processes, but they can indeed cause plentiful porosities, resulting in the uneven Li ion stripping/plating and finally the formation of Li dendrites. Thence, we constructed an atomic interlamellar ion channel by introducing the layered montmorillonite on the surface of the separator to guide Li ion flux and achieved stable Li deposition. The atomic interlamellar ion channel with a spacing of 1.4 nm showed strong absorption capacity for electrolytes and reserved capacity for Li ions, thus promoting rapid transfer of Li ions and resulting in even Li ion deposition at the anode. When assembled with the proposed separator, the Coulombic efficiency of Li||Cu batteries was 98.2% after 200 cycles and stable plating/stripping even after 800 h was achieved for the Li||Li symmetric batteries. Importantly, the proposed separator allows 140% specific capacity increase after 190 cycles as employing the Li–S batteries.