Hybrid Nanocomposites Based on Epoxy/silsesquioxanes Matrices Reinforced with Multi-walled Carbon Nanotubes
Marcelo Alexandre De Farias1  Luiz Antônio Ferreira Coelho1  Sérgio Henrique Pezzin1 
关键词: epoxy resin;    silsesquioxanes;    carbon nanotubes;    hybrid nanocomposite;   
DOI  :  10.1590/1516-1439.023015
来源: SciELO
PDF
【 摘 要 】

The aim of this work was the synthesis of hybrid organic-inorganic epoxy-copolysilsesquioxane nanocomposites reinforced with multi-walled carbon nanotubes (MWCNT). Copolysilsesquioxanes oligomers from 3-aminopropyltriethoxysilane (APTES) and phenyltriethoxysilane (PTES) precursors have been synthesized by a sol-gel process and chemically incorporated to an epoxy resin based on diglycidyl ether of bisphenol A (DGEBA). MWCNT (0.25 wt%) was added to the hybrid matrixes with different degrees of condensation. Fourier transform infrared analysis showed that a high degree of cure was achieved, suggesting that the MWCNT did not affect the curing reaction of the hybrid matrixes. Hybrid nanocomposites obtained by sonication technique presented improvement on thermal stability, exhibiting onset degradation temperatures higher than 340 °C under N2. Tensile tests presented Young’s modulus and maximum stress values up to 2.9 GPa and 47 MPa, respectively, indicating that the new hybrid epoxy/MWCNT nanocomposites show a moderate enhancement of the mechanical properties in comparison with the neat epoxy resin.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License

【 预 览 】
附件列表
Files Size Format View
RO202005130153448ZK.pdf 2332KB PDF download
  文献评价指标  
  下载次数:9次 浏览次数:8次