Study of expanded austenite formed in plasma nitrided AISI 316L samples, using synchrotron radiation diffraction

Materials Research

Marcelo Campos²  Sylvio Dionysio De Souza²  Luis Gallego Martinez¹  Maristela Olzon-dionysio² 

[1] ,Universidade Federal de São Carlos Departamento de Física São Carlos SP ,Brasil

关键词: AISI 316L stainless steel;    plasma nitriding;    expanded austenite;    layer depth;    synchrotron diffraction;    magnetic character;   

DOI  :  10.1590/1516-1439.285914

来源: SciELO

【 摘 要 】

AISI 316L stainless steel samples nitrided at different conditions of temperature and time, showing different properties, such as nitrogen concentration (C N) and nitrided layer thickness, were studied. Expanded austenite (γN) diffraction peaks up to the (222) reflection were observed using suitable wavelength synchrotron radiation. XRD patterns were fitted by Le Bail method, using a special triclinic crystal structure (with a lattice distortion n) for γN, whose peaks were decomposed in a few subpeaks, to consider C N gradient across the nitrided layer. Our results indicate that regarding γN magnetic behavior, which was observed for the samples nitrided at 450 °C, it seems to be correlated not only to high C N (≥31at.%), but also to higher η (≥2.4°), which reaches up to 5.6°. This distortion h decreases when C N increases, consequently, with its minimum close to the surface. On the other hand, for paramagnetic samples (350 °C),η increases up to 1.4° when C N increases up to 30 at.%.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License