Effect of hot pressing variables on the microstructure, relative density and hardness of sterling silver (Ag-Cu alloy) powder compacts

Materials Research

B. Henriques¹  D. Soares¹  J.c. Teixeira¹  F.s Silva¹ 

[1] ,Universidade do Minho Center for Mechanical and Materials Technologies Guimarães,Portugal

关键词: sterling silver;    powder metallurgy;    hot pressing;    microstructure;    density;    hardness;   

DOI  :  10.1590/S1516-14392014005000022

来源: SciELO

【 摘 要 】

The purpose of this work was to investigate the influence of the hot pressing variables, namely pressure, time and temperature, on the microstructure, density and hardness in a sterling silver alloy. Powders were hot pressed under different combinations of pressures (25MPa, 35MPa and 45MPa), times (10 min, 30 min and 60 min) and temperatures (250 ºC, 300 ºC, 400 ºC, 500 ºC and 700 ºC). The microstructures of hot pressed compacts were analyzed by the means of SEM/EDS and optical microscopy. The density and hardness of specimens were assessed. The microstructure of all specimens consisted in Cu-rich precipitates of different sizes dispersed in a Ag-rich matrix. Of the variables that were examined, only temperature produced significant (p<0.05) differences in the density and hardness of the compacts. Full density of powders compacts was achieved for temperatures above 400 ºC, irrespective of the hot pressing time. A hardness peak (~120HV) was observed for the specimens hot pressed at 400 ºC.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License