Synthesis of high value-added zeolitic materials using glass powder residue as a silica source | |
J. A. B. L. R. Alves2  E. R. S. Dantas1  S. B. C. Pergher2  D. M. A. Melo2  M. A. F. Melo1  | |
[1] ,Federal University of Rio Grande do Norte Institute of Chemistry Natal RN ,Brazil | |
关键词: glass powder; zeolite A; zeolite X; | |
DOI : 10.1590/S1516-14392013005000191 | |
来源: SciELO | |
【 摘 要 】
In this work, zeolite A was obtained using alkaline fusion followed by a hydrothermal treatment of glass powder residue derived from the manufacturing of glass. The following parameters were evaluated: leaching of the stock material (silica source), mineralizing agent, alumina source, and the alkaline fusion and crystallization temperatures. The synthesized materials were characterized by chemical analysis using energy dispersive X-ray analysis (EDX), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The XRD and SEM results showed that zeolite A was obtained under almost all of the evaluated parameters. The use of pseudoboehmite as an aluminum source led to the formation of zeolite X as a secondary phase and a change in the temperature of fusion, which at 500 °C, there was formation of zeolite A, hydrated sodalite and zeolite X.
【 授权许可】
CC BY
All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO202005130153063ZK.pdf | 1595KB | download |