Microhardness and EBSD microstructure mapping in partially-pressed al and cu through 90º ECAP die

Materials Research

Alexander P. Zhilyaev¹  Terence G. Langdon¹ 

[1] ,University of Southampton Faculty of Engineering and the Environment Materials Research GroupSouthampton,UK

关键词: equal channel angular pressing;    microstructure;    EBSD;    aluminium;    copper;   

DOI  :  10.1590/S1516-14392013005000037

来源: SciELO

【 摘 要 】

Equal-channel angular pressing (ECAP) is widely recognized as an effective method for processing ultrafine-grained and even nanostructured materials. Important details on processes occurring in the die intersections can be obtained by mapping the microhardness and EBSD microstructures in partially-pressed aluminum and copper through the 90º die of ECAP. Precise measurements were made using grids of partially-pressed Al and Cu and detailed color maps were plotted and compared with EBSD maps. A narrow region along the bisector of two channels reflects altering in microhardness level of the material subjected to simple shear. The microstructural evolution suggests significant refining of the grain structure but there is noticeable inhomogeneity in the microhardness and microstructure for both materials. Factors contributing to the inhomogeneous hardness distribution include the coarse initial grain size, and inhomogeneous deformation across the plane of the die channel intersection due to die wall friction and the formation of a dead zone at the outer corner.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License