Materials Research
Improvement compressive strength of cementitious composites in different curing media by incorporating ZrO2 nanoparticles
Mohammad Hossein Rafieipour2  Ali Nazari1  Mohammad Ali Mohandesi2  Gholamreza Khalaj1 
[1] ,Islamic Azad University Department of Civil Engineering Saveh,Iran
关键词: ZrO2 nanoparticle;    compressive strength;    setting time;    cementitious composite;    curing medium;    limewater;    workability;    TGA;    XRD;    pore structure;   
DOI  :  10.1590/S1516-14392012005000008
来源: SciELO
PDF
【 摘 要 】

In the present work, the effect of curing medium on microstructure, physical, mechanical and thermal properties of ZrO2 nanoparticles blended concrete has been investigated. ZrO2 nanoparticles were partially used instead of cement by 0.5, 1.0, 1.5 and 2.0 weight percent. Curing of the specimens was carried out in water and saturated limewater for 7, 28 and 90 days. The results indicate that ZrO2 nanoparticles up to maximum of 2.0% produces cementitious composite with improved compressive strength by curing in saturated limewater. The optimum level of replacement for the specimens cured in water was 1.0 weight percent. ZrO2 nanoparticles can improve the filler effects and also the high activity of fine particles substantially increases the quantity of strengthening gel. Although the limewater reduces the strength of concrete without nanoparticles when compared with the specimens cured in water, curing the specimens in saturated limewater results in more strengthening gel formation around ZrO2 nanoparticles blended concrete causes high strength.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License

【 预 览 】
附件列表
Files Size Format View
RO202005130152713ZK.pdf 1139KB PDF download
  文献评价指标  
  下载次数:14次 浏览次数:14次