Strain hardening behaviour in forming of sintered iron-0.35% carbon powder metallurgy preform during cold upsetting | |
Sumesh Narayan1  Ananthanarayanan Rajeshkannan1  | |
[1] ,The University of the South Pacific Faculty of Science, Technology & Environment School of Engineering and PhysicsFiji | |
关键词: strain hardening exponent; density hardening exponent; strength coefficient; densification; | |
DOI : 10.1590/S1516-14392011005000074 | |
来源: SciELO | |
【 摘 要 】
A complete experimental investigation on the instantaneous strain-hardening behaviour of powder metallurgy preforms of Fe-0.35%C was carried out. The strain hardening behaviour of the above-mentioned P/M sintered steel preforms with aspect ratio of 0.4 and 0.6, respectively, under triaxial stress state condition was determined by cold upsetting under nil/no and graphite lubricant conditions. The instantaneous strain hardening value (n i), strength coefficient (Ki), and the stress as a function of strain and densification were obtained and analyzed. Further, a relation is obtained from a semi-log plot of stress against relative density. This was analyzed to study the hardening behaviour due to the densification as applied stress is a function of induced strain as well as of densification in the powder metallurgy materials.
【 授权许可】
CC BY
All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO202005130152671ZK.pdf | 1563KB | download |