Polypropylene matrix composites reinforced with coconut fibers

Materials Research

Maria Virginia Gelfuso²  Pedro Vieira Gurgel Da Silva¹  Daniel Thomazini² 

[1] ,Universidade Federal de Itajubá Instituto de Engenharia Mecânica Itajubá MG ,Brazil

关键词: coconut fiber;    composite;    mechanical properties;    polypropylene;   

DOI  :  10.1590/S1516-14392011005000056

来源: SciELO

【 摘 要 】

Polypropylene matrix composites reinforced with treated coconut fibers were produced. Fibers chemically treated (alkalization-CCUV samples) or mechanically treated (ultrasonic shockwave-CMUV samples) were dried using UV radiation. The goal was to combine low cost and eco-friendly treatments to improve fiber-matrix adhesion. Composite samples containing up to 20 vol. (%) of untreated and treated coconut fibers were taken from boxes fabricated by injection molding. Water absorption and mechanical properties were investigated according to ASTM D570-98 and ASTM D638-03, respectively. Electrical characterizations were carried out to identify applications of these composites in the electrical sector. NBR 10296-Electrical Tracking Standard (specific to industry applications) and conductivity measurements were obtained applying 5 kV DC to the samples. CMUV samples containing 5 vol. (%) fiber presented superior tensile strength values (σ~28 MPa) compared to the untreated fibers composite (σ~22 MPa) or alkali treatment (σ~24 MPa). However, CMUV composites containing 10 vol. (%) fiber presented best results for the electrical tracking test and electrical resistivity (3 × 10(7) Ω.m). The results suggest that composites reinforced with mechanically treated coconut fibers are suitable for electrical applications.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License