Performance of 3Y-TZP bioceramics under cyclic fatigue loading | |
Renato Chaves Souza2  Claudinei Dos Santos2  Miguel Justino Ribeiro Barboza2  Carlos Antonio Reis Pereira Baptista2  Kurt Strecker1  Carlos Nelson Elias1  | |
[1] ,Universidade de São Paulo Escola de Engenharia de Lorena Lorena SP ,Brazil | |
关键词: dental materials; 3Y-TZP; mechanical properties; fatigue; | |
DOI : 10.1590/S1516-14392008000100017 | |
来源: SciELO | |
【 摘 要 】
In this work, the static mechanical properties and cyclic fatigue life of 3 mol. (%) Y2O3-stabilized tetragonal zirconia polycrystalline (3Y-TZP) ceramics were investigated. Pre-sintered samples were sintered in air at 1600 °C for 120 minutes, and characterized by X ray diffraction and scanning electronic microscopy. Hardness and fracture toughness were determined by Vicker's indentation method, and Modulus of Rupture was determined by four-point bending testing. Fully dense sintered samples, near to 100% of theoretical density, presented hardness, fracture toughness and bending strength of 13.5 GPa, 8.2 MPa.m½ and 880 MPa, respectively. The cyclic fatigue tests were also realized using four-point bending testing, within a frequency of 25 Hz and stress ratio R of 0.1. The increasing of load stress lead to decreasing of the number of cycles and the run-out specimens number. The tetragonal-monoclinic (t-m) ZrO2-transformation observed by X ray diffraction contributes to the increasing of the fatigue life. The 3Y-TZP samples clearly presents a range of loading conditions where cyclic fatigue can be detected.
【 授权许可】
CC BY
All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO202005130152362ZK.pdf | 809KB | download |