Evaluation of radiopacity and microhardness of composites submitted to artificial aging | |
Diogo Rodrigues Cruvinel2  Lucas Da Fonseca Roberti Garcia1  Luciana Assirati Casemiro1  Luiz Carlos Pardini1  Fernanda De Carvalho Panzeri Pires-de-souza2  | |
[1] ,University of São Paulo School of Dentistry of Ribeirão Department of Dental Materials and ProsthodonticsRibeirão Preto SP ,Brazil | |
关键词: radiopacity; microhardness; composites; artificial aging; | |
DOI : 10.1590/S1516-14392007000300021 | |
来源: SciELO | |
【 摘 要 】
The purpose of this study was to assess the radiopacity and microhardness of different types of resin-based composites (RBC - hybrid; microhybrid; flowable; cement and polyacid modified) before and after being submitted to artificial accelerated aging. Fifty specimens (7 mm in diameter and 2 mm thick) were fabricated, 10 for each material. The specimens were light-cured and submitted to radiopacity and microhardness tests. After obtaining initial radiopacity and microhardness values, the specimens were taken to the artificial accelerated aging, and new measurement of radiopacity and microhardness of the samples was performed. Data were submitted to statistical analysis (Student's t-test - p < 0.05). None of the materials studied showed changes in radiopacity after artificial accelerated aging. There was a significant decrease in microhardness for the microhybrid and polyacid-modified RBC´s. This study suggests that radiopacity remains unaltered after materials are submitted to artificial accelerated aging. Microhardness, however, may vary due to plasticization of the aged RBC matrix.