Hydrolytic degradation of composite resins: effects on the microhardness

Materials Research

Josué Martos²  Prudêncio Willy Rodo Osinaga²  Elisabeth De Oliveira¹  Luis Antônio Suita De Castro¹ 

[1] ,Federal University of Pelotas Pelotas School of Dentistry Department of Clinics and Restorative DentistryPelotas RS ,Brazil

关键词: composite resin;    hydrolytic degradation;    microhardness;   

DOI  :  10.1590/S1516-14392003000400029

来源: SciELO

【 摘 要 】

The purpose of this investigation was to evaluate the microhardness of two laboratory-processed composites (Artglass; belleGlass) and two direct placement composites (Filtek Z250; Alert), after aging in distilled water. Twenty cylinders (8 mm diameter; 2 mm height) per tested material were prepared and stored in 10 ml of distilled water. Five Knoop hardness measurements were made on the surface of the specimens with a Miniload Hardness Tester under a load of 50 g for 30 s at 10 min, 24 h, 30 and 90 days. Statistical analysis was perfomed using two-way ANOVA, followed by a SNK multiple comparison test (p < 0.05). The analysis showed statistically significant difference among hardness means recorded at the different aging time and the tested materials. It may be concluded that all materials presented hydrolytic degradation due to aging in aqueous environment.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License