Mechanical behaviour of copper 15% volume niobium microcomposite wires

Materials Research

Marcello Filgueira²  José Nilson F. De Holanda²  Ruben Rosenthal²  Daltro G. Pinatti¹ 

[1] ,State University of North Fluminense Advanced Materials Laboratory Campos dos Goytacazes RJ ,Brazil

关键词: Cu 15% vol. Nb;    wire drawing;    heat treatments;    anomalous tensile strength;   

DOI  :  10.1590/S1516-14392001000200015

来源: SciELO

【 摘 要 】

Cu-Nb microcomposites are attractive in magnet pulsed field technology applications due to their anomalous mechanism of mechanical strength and high electrical conductivity. In this sense, recently it was conceived the use of Cu 15% vol. Nb wires to operate as a high tensile strength cable for a diamond cutting tool (diamond wires) for marble and granite slabbing. The multifilamentary Cu 15% vol. Nb composite was obtained using a new processing route, starting with niobium bars bundled into copper tubes, without arc melting. Cold working techniques, such as swaging and wire drawing, combined with heat treatments such as sintering and annealing, and tube restacking were employed. The tensile property of the composite was measured as a function of the niobium filaments dimensions and morphology into the copper matrix, in the several processing steps. An ultimate tensile strength (UTS) of 960 MPa was obtained for an areal reduction (R = Ao/A, with Ao-initial cross section area, and A-final cross section area) of 4x10(8) X, in which the niobium filaments reached thickness less than 20 nm. The anomalous mechanical strength increase is attributed to the fact that the niobium filaments acts as a barrier to copper dislocations.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License