Effect of calcium phosphate addition on sintering of El-Oued sand quartz raw materials

Cerâmica

L. Foughali²  A. Harabi²  J. P. Bonnet¹  D. Smith¹  B. Boudaira² 

[1] ,Constantine University Faculty of Exact Science Ceramics Lab,Algeria

关键词: quartz sand;    calcium phosphate;    sintering;    porosity;    cristobalite;    areia de quartzo;    fosfato de cálcio;    sinterização;    porosidade;    cristobalita;   

DOI  :  10.1590/S0366-69132014000400013

来源: SciELO

【 摘 要 】

This work addresses the development of an eventual low cost ceramic insulating or microfiltration membrane supports from inexpensive raw materials such Eloued quartz sand (EQS) and calcium phosphate (CP) using uniaxially dry compaction method. The prepared samples were sintered at different temperatures ranging between 1200 and 1550 ºC. Subsequently, the effects of sintering temperature and amount of CP on samples proprieties were investigated. It is observed that X-ray diffracion measurements confirmed that EQS was transformed into cristobalite and tridymite phases when both sintering temperature and holding time were increased. This transformation is favored with increasing amount of CP, it is observed also formation of CaSiO3 and Ca(Fe)(Al)PO4. The SEM images of the samples sintered at different temperatures illustrate that silica grains, CP grains, intergranular phase contents (Si, Ca, P, and O) and an important open porosity depend on the sintering temperature. The porosity ratio changes in the range between 37% and 34% according to sintering temperature and to CP content; these values are in good agreement with SEM images. The thermal expansion behavior shows a weak expansion in the range of temperature between 600 and 1000 ºC which is situated between 1.27% and 1.33% (variation of 0.05% at 400 ºC).

【 授权许可】

CC BY-NC   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License