Mixing ratio of zinc nitrate and phosphoric acid for preparation of zinc phosphate white pigments | |
H. Onoda1  M. Haruki1  | |
[1] ,Kyoto Prefectural University Department of Informatics and Environmental Sciences Kyoto,Japan | |
关键词: white pigment; zinc phosphates; Zn/P ratio; photocatalytic activity; particle shape; pigmento branco; fosfatos de zinco; proporção Zn/P; atividade catalítica; forma da partícula; | |
DOI : 10.1590/S0366-69132014000300010 | |
来源: SciELO | |
【 摘 要 】
In this work, zinc phosphates were prepared from zinc nitrate and phosphoric acid at various Zn/P ratios as a novel white pigment for use in cosmetics. The chemical composition, powder properties, photocatalytic activity, color phase, moisture retention, and smoothness of the zinc phosphates were studied. Samples prepared at Zn/P = 2/1, 3/2, and 1/1 indicated XRD pattern of Zn3(PO4)2•4H2O. The plane particles were observed in SEM images of sample prepared at Zn/P = 2/1, 3/2 and 1/1. The photocatalytic activity of these zinc phosphate particles was too less to protect the sebum on the skin. The materials prepared at Zn/P = 2/1, 3/2 and 1/1 and their thermal products at 100 °C showed a high reflectance within the range of visible light. Samples prepared at high Zn/P ratio indicated small MIU value.
【 授权许可】
CC BY-NC
All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO202005130132816ZK.pdf | 554KB | download |