Characterization of AlMCM-41 synthesized with rice husk silica and utilization as supports for platinumiron catalysts

Brazilian Journal of Chemical Engineering

J. Chumee²  N. Grisdanurak¹  S. Neramittagapong¹  J. Wittayakun² 

[1] ,Suranaree University of Technology School of Chemistry ,Thailand

关键词: RH-AlMCM-41;    Rice husk;    Phenol hydroxylation;    Pt-Fe;   

DOI  :  10.1590/S0104-66322009000200014

来源: SciELO

【 摘 要 】

RH-MCM-41 was synthesized by using silica from rice husk and further modified to increase acidity by adding Al with grafting method with Si/Al ratio of 75 and 25. The resulting materials were referred to as RH-AlMCM-41(75) and RH-AlMCM-41(25). The XRD spectra of all RH-AlMCM-41 confirmed a mesoporous structure of MCM-41. Surface areas of all RH-AlMCM-41 were in the range of 700-800 m²/g, lower than that of the parent RH-MCM-41, which was 1230 m²/g. After Al addition the Si/Al ratios of RHAlMCM-41(75) and RH-AlMCM-41(25) were higher than that of the parent RH-MCM-41. The RH-AlMCM41 materials were used as supports for bimetallic platinum-iron catalysts, denoted as Pt-Fe/RH-AlMCM-41, with Pt and Fe amounts of 0.5 and 5.0% by weight, respectively. Results from TPR indicated that the presenceof Al might assist the interaction between Pt and Fe as the reduction temperature of iron oxides shifted to a lower value. All catalysts were active for phenol hydroxylation using H2O2 as an oxidant, for which the highest conversions were observed on the RH-MCM-41 material with the highest surface area. The acidity of the supports did not present a significant role in improving the catalytic performance.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License