Brazilian Dental Journal
Surface Treatments for Repair of Feldspathic, Leucite - and Lithium Disilicate-Reinforced Glass Ceramics Using Composite Resin
Christian Alencar Neis1  Nadine Luísa Guimarães Albuquerque1  Ivo De Souza Albuquerque1  Erica Alves Gomes1  Celso Bernardo De Souza-filho1  Victor Pinheiro Feitosa1  Aloisio Oro Spazzin1  Atais Bacchi1 
关键词: dental ceramics;    repairs;    surface treatments.;   
DOI  :  10.1590/0103-6440201302447
来源: SciELO
PDF
【 摘 要 】

The aim of this study was to evaluate the efficacy of different surface conditioning methods on the microtensile bond strength of a restorative composite repair in three types of dental ceramics: lithium disilicate-reinforced, leucite-reinforced and feldspathic. Twelve blocks were sintered for each type of ceramic (n=3) and stored for 3 months in distilled water at 37 °C. The bonding surface of ceramics was abraded with 600-grit SiC paper. Surface treatments for each ceramic were: GC (control) - none; GDB - diamond bur #30 µm; GHF - hydrofluoric acid (10%); GT- tribochemical silica coating (45-μm size particles). Treatments were followed by cleaning with phosphoric acid 37% for 20 s + silane + adhesive. The composite resin was used as restorative material. After repair, samples were subjected to thermocycled ageing (10,000 cycles between 5 °C and 55 °C for 30 s). Thereafter, the samples were sectioned into 1.0 mm2 sticks and tested for microtensile bond strength with 0.5 mm/min crosshead speed. Data were compared by two-way ANOVA and Tukey's test (α=0.05). The superficial wear with diamond bur proved to be suitable for feldspathic porcelain and for leucite-reinforced glass ceramic while hydrofluoric acid-etching is indicated for repairs in lithium disilicate-reinforced ceramic; tribochemical silica coating is applicable to leucite-reinforced ceramic. Predominance of adhesive failures was observed (>85% in all groups). In conclusion, the success of surface treatments depends on the type of ceramic to be repaired.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License

【 预 览 】
附件列表
Files Size Format View
RO202005130110114ZK.pdf 66KB PDF download
  文献评价指标  
  下载次数:13次 浏览次数:14次