Influence of adhesive system and bevel preparation on fracture strength of teeth restored with composite resin
Fábio Herrmann Coelho-de-souza2  Analice Da Cunha Rocha1  Alessandro Rubini1  Celso Afonso Klein-júnior1  Flávio Fernando Demarco1 
[1] ,, Federal University of Rio Grande do Sul Department of Conservative Dentistry Porto Alegre RS ,Brazil
关键词: bevel;    adhesive systems;    fracture strength;    composite resins;   
DOI  :  10.1590/S0103-64402010000400007
来源: SciELO
PDF
【 摘 要 】

The aim of this study was to evaluate the fracture strength of teeth with different cavosurface margin cavity preparations and restored with composite resin and different adhesive systems. Eighty premolars were randomly divided in 8 groups, as follow: G1- sound teeth; G2- MOD preparation (no restoration); G3- Adper Single Bond without bevel preparation (butt joint); G4- Adper Single Bond with bevel preparation; G5- Adper Single Bond with chamfer preparation; G6- Clearfil SE Bond without bevel (butt joint); G7- Clearfil SE Bond with bevel preparation; G8- Clearfil SE Bond with chamfer preparation. The adhesive systems were applied according to manufacturers’ instructions. Composite resin (Filtek Z250) was incrementally placed in all cavities. After 24 h, the specimens were tested in a universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by ANOVA and Tukey’s test (fracture strength) and Fisher’s exact test (fracture pattern). The confidence level was set at 95% for all tests. Prepared and non-restored teeth showed the worst performance and G4 exhibited the highest fracture strength among all groups (p<0.05). In conclusion, all restorative treatments were able to recover the fracture strength of non-restored teeth to levels similar to those of sound teeth. Using a total-etch adhesive system with bevel preparation significantly improved the resistance to fracture.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License

【 预 览 】
附件列表
Files Size Format View
RO202005130109642ZK.pdf 264KB PDF download
  文献评价指标  
  下载次数:5次 浏览次数:9次