Complexation behavior in aqueous edta sol-gel systems for the synthesis of YBa2Cu3O7-x high-temperature superconductors

Journal of the Brazilian Chemical Society

Tran Thi Thuy²  Gerrit Herman¹  Petra Lommens¹  Isabel Van Driessche¹ 

[1] ,Hanoi University of Science and Technology Department of Analytical Chemistry Hanoi,Vietnam

关键词: solution speciation;    superconductor;    YBa2Cu3O7-x;    water-based sol-gel;    edta;   

DOI  :  10.1590/S0103-50532012000700013

来源: SciELO

【 摘 要 】

Two water-based YBa2Cu3O7-x precursor solutions using edta (ethylenediaminetetraacetic acid) as complexing agent are presented. These precursors were employed to deposit thin layers of high-temperature superconducting (HTSC) materials. The influence of the complexation behavior on the formation of transparent and homogeneous solutions and gels after the combination of metal acetates and other modifiers was studied, compared and interpreted using metal-ligand equilibria. The occurrence of different chemical species at different pH values appears to be related to stable gel formation conditions. It is found that both acetic acid and edta play an important role in controlling the condensation reaction to form a continuous network polymer. The precursors were used to deposit textured superconducting thin films on SrTiO3 (STO) substrates by dip coating. Analysis by X-ray diffractometry (XRD) indicated that a single YBCO (yttrium barium copper oxide) phase was obtained. Attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR) was used to determine the carbon residue level in the YBCO final materials, which was lower than 0.01%.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License