Relationship between the dielectric and mechanical properties and the ratio of epoxy resin to hardener of the hybrid thermosetting polymers

Journal of the Brazilian Chemical Society

Newton Luiz Dias Filho¹  Hermes Adolfo De Aquino¹  Geovanna Pires¹  Laércio Caetano¹ 

[1] ,Universidade Estadual Paulista Departamento de Física e Química Ilha Solteira SP ,Brazil

关键词: dieletric relaxation;    dielectric analysis;    epoxy resin;    thermosetting materials;   

DOI  :  10.1590/S0103-50532006000300016

来源: SciELO

【 摘 要 】

The relationship between the dielectric properties (dielectric constant, epsilon', and loss factor, epsilon"; activation energy, Ea) and the ratio of epoxy resin (OG) to hardener of the epoxy resin thermosetting polymers was investigated. The amplitude of the epsilon" peak decreases with increasing OG content until about 73 wt.% and slightly increases at higher OG content. The temperature of the position of the epsilon" peak increases with the increasing of OG content, reaching maximum values for compositions in the range of 67 and 73 wt.%, and then it decreases sharply at higher OG content. The activation energy obtained from dielectric relaxation increased with increasing wt.% OG up to around 70 wt.%. Further increase in concentration of OG up to 83 wt.% reduced Ea. The curves of tensile modulus and fracture toughness mechanical properties as a function of OG content presented a similar behavior.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License