pH Sensitivity of Novel PANI/PVB/PS3 Composite Films

Sensors

Edric Gill²  Arousian Arshak²  Khalil Arshak¹ 

[1]Dept. of Computer and Electronic Engineering, University of Limerick, Limerick, Ireland

[2]Dept. of Physics, University of Limerick, Limerick, Ireland. Tel: [phone], Fax: [phone]

关键词: PANI composite film;    XPS;    thick films;    conductance;    interdigitated electrodes;   

DOI  :  10.3390/s7123329

来源: mdpi

【 摘 要 】

This paper reports on the results from the investigation into the pH sensitivity of novel PANI/PVB/PS3 composite films. The conductimetric sensing mode was chosen as it is one of the most promising alternatives to the mainstream pH-sensing methods and it is the least investigated due to the popularity of other approaches. The films were deposited using both screen-printing and a drop-coating method. It was found that the best response to pH was obtained from the screen-printed thick films, which demonstrated a change in conductance by as much as three orders of magnitude over the pH range pH2-pH11. The devices exhibited a stable response over 96 hours of operation. Several films were immersed in buffer solutions of different pH values for 96 hours and these were then investigated using XPS. The resulting N 1s spectra for the various films confirmed that the change in conductance was due to deprotonation of the PANI polymer backbone. SEM and Profilometry were also undertaken and showed that no considerable changes in the morphology of the films took place and that the films did not swell or contract due to exposure to test solutions.

【 授权许可】

Unknown   
© 2007 by MDPI (http://www.mdpi.org).