Synthesis of Li2Ti3O7 Anode Materials by Ultrasonic Spray Pyrolysis and Their Electrochemical Properties

Materials

Takashi Ogihara¹ 

关键词: spray pyrolysis;    lithium ion battery;    powders;    anode;    oxide;   

DOI  :  10.3390/ma6062285

来源: mdpi

【 摘 要 】

Ramsdellite-type lithium titanate (Li₂Ti₃O₇) powders were synthesized by performing ultrasonic spray pyrolysis, and their chemical and physical properties were characterized by performing Scanning Electron Microscope (SEM), powder X-ray Diffraction (XRD), and Inductively Coupled Plasma (ICP) analyses. The as-prepared Li₂Ti₃O₇ precursor powders had spherical morphologies with hollow microstructures, but an irregularly shaped morphology was obtained after calcination above 900 °C. The ramsdellite Li₂Ti₃O₇ crystal phase was obtained after the calcination at 1100 °C under an argon/hydrogen atmosphere. The first rechargeable capacity of the Li₂Ti₃O₇ anode material was 168 mAh/g at 0.1 C and 82 mAh/g at 20 C, and the discharge capacity retention ratio was 99% at 1 C after the 500th cycle. The cycle performance of the Li₂Ti₃O₇ anode was also highly stable at 50 °C, demonstrating the superiority of Li₂Ti₃O₇ anode materials reported previously.

【 授权许可】

CC BY   
© 2013 by the authors; licensee MDPI, Basel, Switzerland.