Study on Dual Modification of Al-17%Si Alloys by Structural Heredity

Metals

Jing Zhang¹  Hongmei Chen³  Hui Yu²  Yunxue Jin³ 

[1] School of Metallurgy and Materials Engineering, Jiangsu University of Science and Technology, Zhangjiagang 215600, China;School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300132, China; E-Mail:;School of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003, China; E-Mails:

关键词: hypereutectic Al-Si alloys;    dual modification;    structural heredity;   

DOI  :  10.3390/met5021112

来源: mdpi

【 摘 要 】

In this study, Al-17%Si alloys were dual modified by fine-grained structural materials (FSM) according to structural heredity. Microstructure and thermal analyses were undertaken to study the modification effect of the FSM master alloy on primary and eutectic Si. Primary Si is refined to a smaller size and eutectic Si is modified from needle-like to fibrous shape after FSM master alloy addition. The optimal content of FSM master alloy is 20% and the holding time is 15min. Finer FSM master alloy leads to finer Al-17%Si alloy microstructure and more area percentage of α-Al. DSC analyses results show that FSM master alloy can raise the precipitation temperatures of primary and eutectic Si, meanwhile it can reduce the latent heat of Si solidification process.

【 授权许可】

CC BY   
© 2015 by the authors; licensee MDPI, Basel, Switzerland.