Evaluation and Description of Friction between an Electro-Deposited Coating and a Ceramic Ball under Fretting Condition

Materials

Kyungmok Kim¹ 

[1] School of Aerospace and Mechanical Engineering, Korea Aerospace University, 76 Hanggongdaehang-ro, Deogyang-gu, Goyang-si, Gyeonggi-do 412-791, Korea; E-Mail

关键词: fretting wear;    electro-deposited coating;    friction coefficient;    AISI52100;   

DOI  :  10.3390/ma8084778

来源: mdpi

【 摘 要 】

This article describes fretting behavior of zirconia and silicon nitride balls on an electro-deposited coating. Fretting tests are performed using a ball-on-flat configuration. The evolution of the kinetic friction coefficient is determined, along with slip ratio. Experimental results show that the steady-state friction coefficient between ceramic balls (Si₃N₄ and ZrO₂) and an electro-deposited coating is about 0.06, lower than the value between AISI 52100 ball and the coating. After a steady-state sliding, the transition of the friction coefficient is varied with a ball. The friction coefficient for ZrO₂ balls became a critical value after higher fretting cycles than those for Si₃N₄ and AISI 52100 balls. In addition, it is identified that two parameters can describe the transition of the friction coefficient. Finally, the evolution of the friction coefficient is expressed as an exponential or a power-law form.

【 授权许可】

CC BY   
© 2015 by the authors; licensee MDPI, Basel, Switzerland.