Corrosion Behavior in 3.5% NaCl Solutions of γ-TiAl Processed by Electron Beam Melting Process | |
Asiful Hossain Seikh1  Ashfaq Mohammad2  El-Sayed M. Sherif1  Abdulrahaman Al-Ahmari1  | |
[1] Centre of Excellence for Research in Engineering Materials, Advanced Manufacturing Institute, King Saud University, Riyadh 11421, Saudi Arabia; E-Mails:;Princess Fatima Alnijiris’s Research Chair for Advanced Manufacturing Technology (FARCAMT), Advanced Manufacturing Institute, King Saud University, Riyadh 11421, Saudi Arabia | |
关键词: titanium aluminides; corrosion; electron beam melting; polarization; EIS; | |
DOI : 10.3390/met5042289 | |
来源: mdpi | |
【 摘 要 】
In this work, the corrosion behavior of γ-TiAl alloy produced by electron beam melting (EBM) process in 3.5% NaCl solution was reported. The study has been performed using potentiodynamic polarization resistance and electrochemical impedance spectroscopy techniques and complemented by scanning electron microscopy investigations. All measurements were carried out after different periods of alloy exposure in the chloride solutions and at different temperatures. The results showed that the EBM produced γ-TiAl alloy has excellent corrosion resistance confirmed by the high values of polarization resistance and the low values of corrosion current and corrosion rate. With increase in immersion time, the corrosion potential moved to a higher positive value with a decrease in corrosion current and corrosion rate, which suggests an improvement in corrosion resistance. On the other hand, the increase of temperature was found to significantly increase the corrosion of the processed γ-TiAl alloy.
【 授权许可】
CC BY
© 2015 by the authors; licensee MDPI, Basel, Switzerland.
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO202003190002295ZK.pdf | 1123KB | download |