Preparation of Boehmite Sol Employed for Formation of Alumina-Layer over Various Plates with the Dip-Coating

JOURNAL OF CHEMICAL ENGINEERING OF JAPAN

Katsuki Kusakabe¹  Minako Fujii²  Satoshi Kawakami²  Shinya Tanimoto²  Hiromu Hayashi²  Shigeru Sugiyama²  Fumio Shibao¹ 

[1] Department of Applied Chemistry, Graduate School of Engineering, Kyushu University;Department of Chemical Science and Technology, Faculty of Engineering, The University of Tokushima

关键词: Boehmite;    Sol-Gel;    Alumina;    Solid State NMR;    Dip-coating;   

DOI  :  10.1252/jcej.36.1095

来源: Maruzen Company Ltd

【 摘 要 】

References(17)Cited-By(2)Formation of boehmite sol from aluminum isopropoxide in aqueous solution was examined with XRD and solid state NMR to reveal that the hydrolysis of the isopropoxide was completed within a rather short reaction time of 1 h while a longer reaction time of 24 h had been employed in the typical preparation procedure. Although it had been mentioned that γ-alumina was formed from the calcination of boehmite at 1073 K, it was suggested that η-alumina, not γ-type, was obtained after the calcination, based on XRD analyses. In order to develop the employment of boehmite sol as the precursor material, the layer of active alumina and its precursor was formed with the dip-coating technique on glass, stainless steel, magnesia and α-alumina plates to show that approximately 1 μm layers were uniformly formed on glass and stainless steel plates while thickness of the layer formed on magnesia and α-alumina was not estimated due to the reflection of uneven plates of those oxides.