Desulfurization Ability of Metallurgical Dusts from Blast Furnace Ironmaking Process

JOURNAL OF CHEMICAL ENGINEERING OF JAPAN

XIE YUSHENG¹  CHEN YUNFA¹  YE SHUFENG¹  GUO ZHANCHENG¹  YANG XUEMIN¹ 

[1] Institute of Chemical Metallurgy, Chinese Academy of Sciences

关键词: Sulfur Capacity;    Flue Gas;    Desulfurization;    Metallurgical Dusts;    Breakthrough Time;   

DOI  :  10.1252/jcej.34.1103

来源: Maruzen Company Ltd

【 摘 要 】

References(10)Cited-By(3)The sulfur capacity of metallurgical dusts from blast furnace ironmaking processes was measured in the temperature range from 298 to 923 K. The experimental results show that the sulfur capacity of metallurgical dusts is considerably increased with the increase of temperature from 298 to 923 K. The desulfurization ability of metallurgical dusts is mainly depend on its content of oxides of ZnO, PbO, CaO and MnO when the temperature is lower than 623 K, but when the temperature is higher than 623 K the contributions of iron oxides become dominant. Carbon content, due to its absorption effect, has a positive effect on the desulfurization ability of metallurgical dusts below 623 K. If the temperature increased to higher than 623 K the absorption effect of carbon disappears and the role of desulfurization reaction between H2S and the metal oxide such as ZnO, PbO, Fe2O3, CaO and MnO as well as the H2S diffusion in intraparticle of metallurgical dusts seems more important.

【 授权许可】

Unknown