Effects of Dry Grinding of Powder Mixture on Formation of Forsterite in Sintered Body and Its Mechanical Properties

JOURNAL OF CHEMICAL ENGINEERING OF JAPAN

Fumio Saito¹  Mitsuru Nikaido²  Shigeru Sano²  Yu-ichi Yoshizawa³ 

[1] Institute for Advanced Materials Processing, Tohoku University;Chemical Engineering Department, Ichinoseki National College of Technology;Government Industrial Research Institute of Nagoya

关键词: Grinding;    Forsterite;    Talc;    Bending Strength;    Tumbling Ball Mill;   

DOI  :  10.1252/jcej.33.709

来源: Maruzen Company Ltd

【 摘 要 】

References(14)Cited-By(3)Dry grinding of a powder mixture composed of talc and magnesium carbonate was conducted using a tumbling ball mill to investigate formation of forsterite in bodies sintered from the ground mixture and their bending strengths. The grinding causes a structural change in the starting materials from a crystalline state to an amorphous one. The amorphous mixture leads to the formation of single-phase forsterite at relatively low sintering temperature, at which the bending strength of the sintered bodies reaches the maximum value. The maximum bending strength increases with increasing grinding time for the mixture. The sintering temperature providing the maximum bending strength becomes low as grinding progresses. Dry grinding for the mixture is favorable for production of forsterite ceramics.

【 授权许可】

Unknown