Preparation of Fe Oxide and Composite Ti-Fe Oxide Ultrafine Particles in Reverse Micellar Systems

JOURNAL OF CHEMICAL ENGINEERING OF JAPAN

Jun-ya Mizumoto¹  Susumu Shiojiri¹  Isao Komasawa¹  Takayuki Hirai¹ 

[1] Department of Chemical Science and Engineering, Graduate School of Engineering Science, Osaka University

关键词: Reverse Micelle;    Ultrafine Particle;    Iron Oxide;    Titanium Dioxide;    Composite Particle;   

DOI  :  10.1252/jcej.30.938

来源: Maruzen Company Ltd

【 摘 要 】

References(13)Cited-By(7)Fe oxide and composite Ti-Fe oxide ultrafine particles have been prepared using sodium big (2-ethylhexyl) suffosoccinate (Aerosol OT; AOT)/isooctane reverse micellar solutions. Fe2O3 particles were prepared by mixing a miceller solution containing sulfuric acid solution of ammonium irom (III) sulfate with an “alkaline” or a “neutral” micellar solution containing NaOH solution or distilled water, respectively. The formation of TiO2 particles by adding titanium tetrabutoxide (TTB) to a micellar solution was also facilitated by NaOH. Simultaneous feeding of both TTB and Fe3+ solutions did not form composite particles but only Fe2O3 particles, indicating that the presence of Fe3+ prevented the formation of cores of TiO2. The TiO2 particles were thus prepared at first in the micellar solution, to which Fe3+-containing micellar solution was fed. The resulting particles possibly have a structure in which TiO2 particles are coated by Fe2O3 thin layer.

【 授权许可】

Unknown