EFEITO DA ESPESSURA E DO VÃO NA DEFORMAÇÃO EM FLEXÃO DE PAINÉIS DE MADEIRA

CERNE

Menezzi, Cláudio Henrique Soares Del¹  Gonçalez, Joaquim Carlos¹  Pazetto, Valéria Maria de Figueiredo¹ 

[1] Universidade de Brasília, Brasília, Brazil$$

关键词: Deflection;    Mechanical testing;    Dimensioning of parts.;   

DOI  :  10.1590/01047760201521041873

来源: Universidade Federal de Lavras-UFLA

【 摘 要 】

This study aimed to evaluate the correlation between the physical and mechanical properties of MDF (Medium Density Fiberboard) and MDP (Medium Density Particleboard) used in furniture manufacturing. The physical properties density and moisture content and the mechanical properties static bending (MOE and MOR) were determined. The experiment was made with three panel thicknesses (15 mm, 18 mm and 25 mm) and three different spans with relationship L/h (span divided by thickness) of 30, 35 and 40 totaling nine treatments for each type of panel with three replications. These samples were subjected to nondestructive bending test, with loads equivalent to 25 g.cm-² uniformly distributed in conditioned environment (temperature 20º C ±1, humidity 65% ±1). The final deformation load was recorded after a week, and the residual deformation, after removal of the load, was also registered. Statistical analysis of the results evaluated the effect of treatments relative to the span and thickness. The analysis showed significant differences between the results for each thickness, however, the span demonstrated greater influence than the thickness. Among the sample sizes evaluated the best value found was L/h = 30.

【 授权许可】

Unknown