Bulletin of the Korean chemical society | |
Poly(vinylbenzyl chloride-glycidyl methacrylate)/Polyethylene Composite Anion Exchange Membranes for Vanadium Redox Battery Application | |
Kyoung-Hee Shin1  Se-Kook Park1  Min-A Park1  Joonmok Shim1  Jae-Deok Jeon1  Ki Bong Lee1  Chang-Soo Jin1  | |
关键词: Vanadium redox battery; Anion exchange membrane; Vinylbenzyl chloride; Glycidyl methacrylate; | |
DOI : | |
学科分类:化学(综合) | |
来源: Korean Chemical Society | |
【 摘 要 】
Anion exchange membranes for a vanadium redox flow battery (VRB) were prepared by pore-filling on a PE substrate with the copolymerization of vinylbenzyl chloride (VBC) and glycidyl methacrylate (GMA). The ion exchange capacity, water uptake and weight gain ratio were increased with a similar tendency up to 65% of GMA content, indicating that the monomer improved the pore-filling degree and membrane properties. The vanadium ion permeability and open-circuit voltage were also investigated. The permeability of the VG65 membrane was only 1.23 × 10−7 cm2 min−1 compared to 17.9 × 10−7 cm2 min−1 for Nafion 117 and 1.8 × 10−7 cm2 min−1 for AMV. Consequently, a VRB single cell using the prepared membrane showed higher energy efficiency (over 80%) of up to 100 cycles compared to the commercial membranes, Nafion 117 (ca. 58%) and AMV (ca. 70%).
【 授权许可】
Unknown
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO201912010244562ZK.pdf | 685KB | download |