Synthesis and Photoelectronic Properties of Thermally Stable Poly[oxy(2,7-fluoren-9-onenylene)oxy(diorganosilylene)]s

Bulletin of the Korean chemical society

Young Tae Park¹  Eun Ae Jung¹ 

关键词: Poly[oxy(2;    7-fluoren-9-onenylene)oxy(diorganosilylene)]s;    Absorption;    Excitation;    Fluorescence;    Thermal stability;   

DOI  :  

学科分类：化学（综合）

来源: Korean Chemical Society

【 摘 要 】

Melt copolymerization reactions of several bis(diethylamino)silane derivatives, bis(diethylamino)methylphenylsilane, bis(diethylamino)methyloctylsilane, 1,2-bis(diethylamino)tetramethyldisilane, and 1,3-bis(diethylamino) tetramethyldisiloxane, with 2,7-dihydroxyfluoren-9-one were carried out to yield poly[oxy(2,7-fluoren- 9-onenylene)oxy(diorganosilylene)]s bearing the fluoren-9-one fluorescent aromatic group in the polymer main chain: poly[oxy(2,7-fluoren-9-onenylene)oxy(methylphenylsilylene)], poly[oxy(2,7-fluoren-9-onenylene) oxy(methyloctylsilylene)], poly[oxy(2,7-fluoren-9-onenylene)oxy(tetramethyldisilylene)], and poly[oxy- (2,7-fluoren-9-onenylene)oxy(tetramethyldisiloxanylene)]. These polymeric materials are soluble in common organic solvents such as CHCl3 and THF. FTIR spectra of all the materials reveal characteristic Si-O-C stretching frequencies at 1012-1018 cm−1. In the THF solution, the prepared materials show strong maximum absorption peaks at 258-270 nm, strong maximum excitation peaks at 260-280 nm, and strong maximum fluorescence emission bands at 310-420 nm. TGA thermograms suggest that most of the polymers are essentially stable to 200 °C without any weight loss and up to 300 °C with only a weight loss of less than 5% in nitrogen.

【 授权许可】

Unknown